AS2700接著密封膠 Adhesive
FEATURE(產品簡介)
- 10 : 1 VOLUMETERIC RATIO FOR MACHINE OR CARTRIDGE DISPENSING
- VERY FAST ROOM TEMP CURE
- 20 MINUTES OF WORKING TIME AT ROOM TEMPERATURE
- GOOD ADHESION TO MOST SUBSTRATES
DESCRIPTION(產品簡介)
2 PART RTV SILICONE ADHESIVE SEALANT PASTE NON CORROSIVE FAST CURE
參數表PARAMETERS
- CODE
AS2700
- FEATURE 1
10 : 1 volumeteric ratio for machine or cartridge dispensing
- FEATURE 2
Very fast room temp cure
- FEATURE 3
20 minutes of working time at room temperature
- FEATURE 4
Good adhesion to most substrates
- APPEARANCE
Thixotropic paste
- TEST CONDITIONS
After 7 days cure at 23°+/-2°C and 50+/-5% humidity
- COLOUR
Grey
- COLOUR A PART
White
- COLOUR b PART
Black
- SG
1.25
- MIN WORKING TEMP - °C
-50°C
- MAX WORKING TEMP +°C
200 °C
- FDA
NO
- SHELF LIFE
12mths
- MIN STORAGE TEMPERATURE °C
-5 °C
- MAX STORAGE TEMPERATURE °C
+ 30°C
- PACK TYPE
2-PART
- MIX RATIO
10:1
- RHEOLOGY
Paste
- VISCOSITY A-PART MPAS
380000 mPas
- VISCOSITY B-PART MPAS
26000 mPas
- VISCOSITY MIXED PART MPAS
342000mPas
- NON CORROSIVE
YES
- CURE TYPE
Condensation
- RTV OR HEAT CURE
RTV
- SELF BONDING
Yes
- UL 94V-0
NO
- DURO SHORE A
39
- Tensile MPa
2MPa
- ELONGATION %
232%
- EXTRUSION RATE G/MIN
105 g/min
- MODULUS YOUNGS MPA
0.87MPa
- CTE VOLUMETRIC PPM/°C
768ppm/°C
- CTE LINEAR PPM/°C
256 ppm/°C
- TACK FREE TIME MINS
20mins
- MAX CURE MINS @ 25 °C
0.83hrs
- THERMAL CONDUCTIVITY W/MK
0.3W/mK
- VOLUME RESISTIVITY OHMS CM
> 1.1E+14 ohms cm