SILCOSET 158接著密封膠 Adhesive

FEATURE(產品簡介)
  • HIGH TEMPERATURE RESISTANCE
  • ROLLS ROYCE AEROSPOACE APPROVED
  • RESISTANT TO SOLVENTS AND CHEMICALS
  • EXCELLENT ADHESION TO MOST SUBSTRATES
DESCRIPTION(產品簡介)

1 PART RTV SILICONE ADHESIVE SEALANT PASTE HIGH TEMPERATURE

索取樣品
參數表PARAMETERS

  • CODE

    Silcoset 158

  • FEATURE 1

    High temperature resistance

  • FEATURE 2

    Rolls Royce Aerospoace approved substrates

  • FEATURE 3

    Resistant to solvents and chemicals

  • FEATURE 4

    Excellent adhesion to most substrates

  • APPEARANCE

    Translucent paste

  • TEST CONDITIONS

    After 7 days cure at 23°+/-2°C and 60+/-5% humidity

  • COLOUR

    Black paste

  • SG

    1.07

  • MIN WORKING TEMP - °C

    -60 °C

  • MAX WORKING TEMP +°C

    300°C

  • FDA

    No

  • SHELF LIFE

    24mths

  • MAX STORAGE TEMPERATURE °C

    40 °C

  • PACK TYPE

    1-Part  

  • RHEOLOGY

    Paste

  • NON CORROSIVE

    NO

  • CURE TYPE

    Acetoxy

  • RTV OR HEAT CURE

    RTV

  • SELF BONDING

    Yes

  • DURO SHORE a

    38

  • HARDNESS IRHD

    38

  • TENSILE MPA

    2.32MPa

  • ELONGATION %

    290%

  • TEAR KN/M

    5.5 kN/m

  • EXTRUSION RATE G/MIN

    270g/min

  • MODULUS YOUNGS MPA

    0.7 MPa

  • MODULUS @ 100% STRAIN MPA

    0.94 MPa

  • LINEAR SHRINKAGE %

    0.8%

  • MAX CURE HRS @ 25 °C

    7HRS

  • THERMAL CONDUCTIVITY W/MK

    0.2 W/mK

  • TACK FREE TIME MINS

    4MINS

  • VOLUME RESISTIVITY OHMS CM

    >1E+16 ohms cm

  • surface RESISTIVITY OHMS CM

    >3.57E+15 ohms cm

  • CTE VOLUMETRIC PPM/°C

    924ppm/°C

  • CTE LINEAR PPM/°C

    308ppm/°C

  • DIELECTRIC STRENGTH KV/MM

    18 kV/mm

  • DIELECTRIC CONSTANT @ 1KHZ

    3

  • DISSIPATION FACTOR @ 1KHZ

    0.0025

  • LAP SHEAR ALUMINIUM KG/CM²

    10.01g/cm²